Corrosion-resistant chemical topcoat, steel structure anti-corrosion paint, acid and alkali resistant primer.

Epoxy Resin Topcoat

[Product Description]

Epoxy resin topcoat is a two-component anticorrosive paint composed of epoxy resin, pigments and fillers, additives, solvents, etc., and is used in conjunction with a curing agent.

Also known as: epoxy anticorrosive topcoat, epoxy anticorrosive finish, epoxy high-build anticorrosive topcoat, epoxy coating, epoxy high-build coating, epoxy high-build anticorrosive coating, epoxy protective coating, epoxy high-build protective coating, epoxy anticorrosive coating, epoxy resin paint, epoxy resin topcoat, epoxy resin coating, epoxy resin anticorrosive paint, epoxy resin anticorrosive topcoat, epoxy resin anticorrosive coating.

[Basic Parameters]

◆Brand: Whale

◆Product Name: Epoxy Resin Topcoat

◆Product Model: H06-9

◆Packaging Specification: 24+4

◆Component Ratio: 6:1

◆Film Color: Various colors

◆Flash Point: Approximately 29°C

◆Application Method: Spraying, Roller Coating, Brush Coating

[Main Characteristics]

◆Strong Adhesion: Epoxy primer has excellent adhesion, firmly bonding to most substrates without film peeling.

◆Excellent Mechanical Properties: Hardness, flexibility, impact resistance, etc., meet standards.

◆High Solid Content: The coating has a high solid content.

◆Excellent Anticorrosive Properties: Good resistance to water, oil, solvents, acids, alkalis, seawater, salt spray, and other corrosive conditions.

[Product Usage]

Suitable for coating steel bridges, concrete, containers, chemical storage tanks, offshore platforms, ships, port facilities, and environments with severe corrosion conditions.

[Basic Parameters]

◆Specific Gravity: Approximately 1.20 kg/L (after mixing)

◆Pot Life (23±2°C): 8 hours

◆Condition in Container: After stirring and mixing, no hard lumps, uniform state.

◆Dry Film Thickness: Approximately 100 μm

◆Theoretical Consumption: Approximately 220 g/m² (based on 60 μm dry film, excluding loss)

◆Drying Time: Surface dry ≤1h, hard dry ≤24h, fully cured 7d

◆Induction Time: 0.5h (23°C±2°C)

◆Recoat Interval: Substrate Temperature 5°C 20°C 30°C

Minimum 48h 24h 12h

Maximum 7d 7d 7d

[Compatible Topcoats]

Epoxy topcoat, chlorinated rubber paint, epoxy asphalt paint, acrylic polyurethane paint, polyurethane paint, chlorosulfonated paint, fluorocarbon paint.

[Surface Treatment]

◆Steel surface blast cleaning to Sa2.5 grade, surface roughness 30μm-75μm.

◆Power tool cleaning to St3 grade.

◆For surfaces coated with primer, use light sweep blasting or pneumatic (electric) tools for secondary grinding.

[Application Conditions]

◆Substrate temperature must be above 3°C, relative humidity must be below 85%.

◆Steel plate temperature should be at least 3°C above dew point. In summer, under direct sunlight, recoating should be completed within 5 days; beyond 5 days, sand the surface for adhesion.

◆When the substrate temperature is below 5°C, the curing reaction between epoxy resin and curing agent stops or slows down, so application is not recommended.

[Application]

[Precautions]

◆Epoxy paint should not be directly used with alkyd paint to avoid saponification reaction and film peeling.

◆Steel surfaces must be blast-cleaned; simple grinding and rust removal are not ideal.

◆Do not apply in heavy wind, rain, snow, or when air humidity is above 85%.

◆During application in high-temperature seasons, dry spraying may occur. To avoid dry spraying, adjust with thinner until no dry spraying occurs.

◆Curing period: 20°C, 7 days or more.